Decolak Catalytic 501
Decolak Basic 201


Protects wood and brings it to life

Lacquer manufacturersPolystick provides comprehensive wood care solutions. Dekolak is a dual-component multi-layered lacquer based on polyurethane for application on wood veneer or full wood. It is used together with Decolak Basecoat 201. The lacquer creates a smooth and long-lasting protective surface over the wood.

Product Specifications
Degrees of Gloss
15%, 20%, 35%, 50%
Decolak 501
Mix Ratio
1:2 (1 part hardener to 2 parts lacquer)
Viscosity in Container (DIN 4 cup)
37 seconds at 20º C
Viscosity at Work (DIN 4 cup)
14-16 seconds at 20º C
Work Time (after mixing)
Around 2 hours
Gravity, Suction-Fed Spraying
Work Pressure/ Nozzle Aperture
Gravity-Fed Spraying (Cup)
2.5-3 bar/ 1.4-1.8 mm
Suction-Fed Spray (Airless)
5 bar/ 0.9mm diameter
Quantity of lacquer in spraying
120-140 gm per sq.m
Drying Time at 20º C
Drying Time - dust
Around 20 minutes
Touch-dry time
Around 40 minutes
Drying Time - sanding
5-6 hours
Lacquer Product Life
12 months
Hardener Product Life
12 months
Creates a protective layer over wood to prevent abrasion and wear.

Work Instructions
Lacquer manufacturersrecommendations: The foundation must be clean and dry, with no loose parts. It is advisable to use work gloves and ventilate the workplace while using this material.

To prepare a 1-liter lacquer mixture that is ready for application: mix 1/2 liter Lacquer 301 with 1/4 liter Hardener 501 and 1/4 liter of Thinner 11 (at a work temperature of 18-20º C).

Download Our Safety Data Sheet (MSDS)

Note: The above information is based on Polystick´s best knowledge as lacquer manufacturers and is intended to provide general data only concerning its products and usage. Consequently the company is not liable as a guarantor regarding a product´s specific features or its suitability for particular applications. It is recommended that all work be preceded by tests in the work environment and with the intended materials to achieve optimal implementation.